Development of a high strength and ductile Nb-bearing dual phase steel by cold-rolling and intercritical annealing of the ferrite- martensite microstructures
|
|
نوع پژوهش
|
مقاله چاپشده در مجلات علمی
|
|
کلیدواژهها
|
,Dual phase steel ,Cold-rolling ,Intercritical annealing ,Niobium Grain refinement
|
|
چکیده
|
Dual phase(DP)steelscontainingdifferentamountsofNbmicroalloyingelementwereproducedbycold- rolling followedbyintercriticalannealingofaferrite-martensiteduplexstartingstructure.Theeffectsof Nb contents(0.00,0.06,0.12and0.18wt%)andintercriticalannealingtimeonthemicrostructural evolutions andmechanicalpropertieswerestudied.Resultsfrommicroscopicimagesshowedthatin- creasing Nbcontentincreasedthevolumefractionofmartensiteanddecreasedtheaveragegrainsizeof ferrite. Tensileresultsillustratedanexcellentstrength-elongationbalanceintermsofenergyabsorption (160Jcm3) andtoughness(229MPa).Thelowestgrainsizeofabout1.4070.37 mmwasachievedinthe DP steelcontaining0.12wt%Nbwhosestrengthwasabout123%higherthanthatoftheas-received ferritic-pearlitic steel(e.g.540MPa),withoutlossofductility.Thevariationsofstrength,elongationand fracturemechanismofthespecimenswithNbcontentsandintercriticalannealingtimewerecorrelated to themicrostructuralfeatures
|
|
پژوهشگران
|
علی قاطعی کلاشمی (نفر اول)، احمد کرمانپور (نفر دوم)، عباس نجفی زاده (نفر سوم)، یوسف مظاهری رودبالی (نفر چهارم)
|